PL-RSCKF Recrystallized Silicon Carbide (RSIC) Kiln Furniture
Descripción
PL-RSCKF Recrystallized Silicon Carbide (RSIC) Kiln Furniture
1. Properties and applications:
RSiC material is made of a select grade and high-purity silicon carbide powder without any additive composition, consolidated by vacuum induction sintering furnace at temperature 2450c. This material is with high antioxidant ability, low mass and high temperature strength, long life, size stability, load-bearing ability under high temperature and good energy-saving effects, many products such as rollers, beams, plates, temperature-measuring pipes, nozzles for burners, cooling air pipes and other shaped structural parts can be made from it, which are widely used in Roller kiln, Tunnel kiln, Shuttle kiln & Bell kiln for ceramics, electric porcelain, metallurgy industries etc.
2. Specifications:
Recrystallized Silicon Carbide (RSIC)
Properties Units R-SIC
α-SIC Composition Vol％ ≥99.5
Si3N4 Composition Vol％ 0
Free Si Composition Vol％ 0
Density g/cm3 2.7
Apparent Porosity ％ 15.5
Modulus Of Rupture @20℃ MPa 91-101
Modulus Of Rupture @1200℃ MPa 109
Modulus Of Rupture @1350℃ MPa 119
Modulus Of Crushing @20℃ MPa 299
Thermal Conductivity @1200℃ w.m-1.k-1 36.5
Thermal Expansion @1200℃ a x 10-6/ ℃ 4.70
Thermal Shock Resistance Best
Max working Temperature ℃ 1650
1. Properties and applications:
RSiC material is made of a select grade and high-purity silicon carbide powder without any additive composition, consolidated by vacuum induction sintering furnace at temperature 2450c. This material is with high antioxidant ability, low mass and high temperature strength, long life, size stability, load-bearing ability under high temperature and good energy-saving effects, many products such as rollers, beams, plates, temperature-measuring pipes, nozzles for burners, cooling air pipes and other shaped structural parts can be made from it, which are widely used in Roller kiln, Tunnel kiln, Shuttle kiln & Bell kiln for ceramics, electric porcelain, metallurgy industries etc.
2. Specifications:
Recrystallized Silicon Carbide (RSIC)
Properties Units R-SIC
α-SIC Composition Vol％ ≥99.5
Si3N4 Composition Vol％ 0
Free Si Composition Vol％ 0
Density g/cm3 2.7
Apparent Porosity ％ 15.5
Modulus Of Rupture @20℃ MPa 91-101
Modulus Of Rupture @1200℃ MPa 109
Modulus Of Rupture @1350℃ MPa 119
Modulus Of Crushing @20℃ MPa 299
Thermal Conductivity @1200℃ w.m-1.k-1 36.5
Thermal Expansion @1200℃ a x 10-6/ ℃ 4.70
Thermal Shock Resistance Best
Max working Temperature ℃ 1650